Mankind has taken a huge leap and totally changed the way of life and also welding have been most significant reasons which may have allowed him to beat the world and grow quite possibly the most dominant species. The reasoning behind regarding welding is reasonably simple where two or more work pieces mainly metals or another alloys are welded or joined together by making use of a molten solution forming the bridge between the two. There are plenty of welding techniques adapted for different sorts of requirements. MIG (Metal Inert Gas) welding way is one in every of. Welding aluminum is utilizing MIG welding technique is different then MIG welding.

The above statement is pretty much true as everything may go wrong while welding steel this also factor may be magnified while welding aluminum. Even something as small as argon flow rate makes a huge difference and makes a contribution to the welders vows. All you’ll ever should use is a little deviation or obstruction and everything can go wrong in seconds. A bit of burr over the copper tip causes the wire feed to curtail and burn to the top.

Important matters bear in mind for MIG welding Aluminum:

1. Using of Spool Gun is absolutely significant. It avoids frustrations to significant levels. You cant ever feed soft aluminum wire.
2. Look into that you really push the puddle rather than pull it for any cleaner soot free weld.
3. Use the longer stand out. MIG welding aluminum uses spray transfer plus the wire never reaches the puddle. Longer stick out would suffice for the problem when it avoids possible burn backs.
4. Always see to that that you employ argon and not argon carbon-dioxide mixture. Even argon helium mixture is fine. If you do not need to cussing do not use argon carbon-dioxide mixture.

Machine and Spool Gun Settings:

1. That you are impossible to use MIG welder that’s thinner than 1/8″. As being a good MIG aluminum welder you might consider be capable to weld as thin as 0.070.
2. For Thicker aluminum pieces say probably around 1/4″ to 5/16″, using 3/64 inch wire feed with 26-27 volts and 400-425 RPM of wire feed would suffice for the job in hand. For thicknesses in between 1/8″ and 5/16″ you can make use of 23 volts and 300 ipm.
3. The wire speed setup should be slightly higher than what you think it should be to avoid burning of the welding tips.
4. Ipm represnts inches per minute. How are you supposed to find out what’s the best ipm for the job? Just pull the trigger and count the seconds as thousand one, thousand two before you 6. Measure the wire that came out and round it up to the nearest whole inch and add a zero. For example, if it’s 35 inches, you have 350 ipm.
5. Get some scrap and fine tune the settings till you get the results you want as every machine varies to others.

About the Author

Cameron Ward works for the inverter welder peak body educating the community about new innovations in welding technology. Cameron may be reached via email at ward.cam1001@yahoo.com. If you have any questions about tig welders machines and their design please don’t hesitate to email me.